High-strength Non-shrinkage Grouting Material

Introduction
Polar Bear Non-Shrink grouting material is blended through a special procedure by specially selected cementitious material, carefully selected fine aggregate and admixture. It owns the characteristics of high flow, non-shrinkage, early strength and high strength. Functionally they are divided into two categories include four products: High strength -Ⅰ,-Ⅱ; Extra early strength-Ⅰ,-Ⅱ.
Properties

 

   1.  Double expansion in plastic and hardened state, compensate the dry shrinkage, ensure the fixed combination between

        steel-back plane and concrete base, efficiently transmit the load carrying into the base.

   2.  High early strength: this material is obtained by special cement as its basic material, it is suitable for urgent repair and

        accelerators construction under negative temperature environment.

   3.  High fluidity.

   4.  Easily used, only mixed with water on site, easily pumped.

   5.  Durability: High final strength, excellent impermeability and corrosion resistance, ensure accuracy of equipment

        setting.

   6.  Working environment: this material can be operated in a negative temperature environment with a rapidly

        increased strength.

   7.  Non-chloride: no harm for equipment or armature reinforcement
 

  • Data

     

    Name

    HS-Ⅰ

    HS -Ⅱ

    HS -Ⅲ

    EES-Ⅰ

    EES-Ⅱ

    EES-Ⅲ

    Grain size

    4.75mm,﹪

    ≤2.0

    Setting time(min)

    Initial

    ≥120

    ≥45

    ≥30

    Bleeding capacity/%

    ≤1.0

    Fluidity /mm

    Initial

    ≥270

    ≥320

    20min

    --

       --

    --

    --

    ≥230

    30min

    ≥230

    --

    Compressive

    (Mpa), ≥

    2h

    --

    --

     

    --

    --

    ≥20.0

    4h

    --

    --

     

    ≥30

    ≥20.0

    --

    1d

    ≥35.0

    ≥22.0

    ≥20.0

    ≥50.0

    ≥40.0

    ≥55.0

    3d

    ≥55.0

    ≥40.0

    ≥40.0

    ≥55.0

    ≥50.0

    ≥60.0

    28d

    ≥80.0

    ≥70.0

    ≥60.0

    ≥70.0

    ≥70.0

    ≥70.0

    Height change %

    1d

    ≥0.020

    Bond strength (MPa)

    28d

    ≥4.0

    Steel Corrosion

    No steel corrosion

    W/C

    0.14

    0.15

    0.14

    0.14

    0.15

    0.14

    Operating temperature

    Above 0℃

    Above 5℃

    Above -15℃

    Above -10℃

    Above -5℃

  • Application

     

    1. Heavy equipment, High precision grinder.

    2. Erection Engineering of Structural steel.

    3. Grouting to column foundation, pile foundation and Rock foundation to fixation.

    4. Anchoring of frame structure joint.

    5. Repair to the honey-comb and holes of reinforced concrete structure.

    6. Repair & Reinforcement to concrete structure.
     

Method

 

Foundation treatment:

1. Scaling and cleaning will be applied to the concrete base

2. Solvent should be adopted to clear up the rust and oil on the bottom (the surface that will contact

    grout) of equipment

3. Molding board joint should be treated well to ensure grouting material won’t leak.

4. Before grouting ,keep the concrete bed wet without water.


Mixing:

1. Pour required amount water into the barrel first, then add a bag of material stir for about 5

    minutes.

2. When stirring, the stir vane should move up and down, left and right along the barrel side in order

    to make the materials adhered to the bottom and side involved in mixing operation. The stir vane

    is not allowed to be above the mixture to avoid the invasion of air.

3. If grout thickness more than 100mm, 5-10mm clean crushed stone should be added.

4. Ensure enough mixing ability for continuous operating.


Grouting:

1. Mixed grouting material should be used out before lost its fluidity.

2. Grouting should begin from one side intend to avoid release entrapped air.

3. Coordinating mixing ability with grouting speed well for continuous operating.

4. Grouting surface should be a little higher than designed peak. In case of not need this part, it

    can remove before hardening.


Curing:

Ahead of hardening, all the uncovered parts should be cured well according to the concrete curing demand.


Shelf life:

6 months for High strength and 3months for Extra early strength
 

Storage
Package
Grouting material 25kg/bag
Consumption
Mixed paste bulk 12.5L/bag, Weight per cubic meter 2200kg
Images

◇   Tangshan Xinxing Steel Co.,Ltd                             ◇   Liaoning Yingkou Qinghua refactory Co.,Ltd

◇   Shunxing Steel Co.,Ltd                                            ◇   Qinhuangdao Qianye cement plant

◇   Qian'an capital steel Co.                                         ◇   Beijing Aviation Group building construction project Co.,Ltd

◇   Beijing The third Cogeneration Plant                   ◇    Hebei Lanbei Wine corp.

◇   Beijing Qinghe clean water treatment plant        ◇   Jidong cement plant

◇   Shan'xi electric third branch                                    ◇   Fuxin Qinghe Power plant

◇   China Building engineering Corp.                        ◇   Liaoning power plant

◇   Tangshan Sanyou Thermal power plant             ◇   Northeast electric second branch

Download

Online Service - English

Simon Mu:
Jack Young:
Julia Zhou:

Online Service - Russian

Цянь бинь Чжоу: