Introduction

The product obtained by grinding sulphoaluminate cement clinker, consisting of essentially anhydrous calcium sulphoaluminate. Suitable gypsum shall be blended with clinker during manufacture of low-alkalinity cement. The product has low alkalinity and small free expansion property. It is hydraulicity binding material. The code no is L-SAC.

The product carries out the standard: JC/T659-1997. The strength grade depends on its7 days compressive strength. There are three grades: 32.5, 42.5 and 52.5.

The product achieved a class second provincial prize of excellent new product, a class third provincial prize of improvement science and technology.

It is one of important new product of state. The item code is 98G041F6200009.

Properties

Besides the high early-strength property as rapid-hardening cement, low alkalinity cement has some other characteristics such as low alkalinity、

small expansive ratio、short stability time、and small dry-shrinkage rate, compounded with glass fiber. It has high strength retaining ratio and longer

work-time, so it is the special cement for making GRC products.

Data

1. Specific surface area: ≥400m²/kg.

2. Setting time:

Initial setting time: ≥25 min.

Final setting time: ≤180 min.

3. Alkalinity

To the cement paste under the condition C/W=10:1, the PH after hydrating 1 hour is less than 10.5.

4. Free expansive ratio:

Under the condition cement/sand=1:0.5, the free expansive ratio is 0.00%-0.15% in 28 days.

5. The strength in different age are not less than the following:

Grade	Compressive strength (Mpa)		Bending strength (Mpa)
Grade	1d	7d	1d	7d
32.5	25.0	32.5	3.5	5.0
42.5	32.0	42.5	4.0	5.5
52.5	39.0	52.5	4.5	6.0

Application

The cement can be used to produce light-weight complex slab of internal and external wall, and GRC products such as corrugated tile, net-frame

slab, ventilation duct, and some other structures.